國產(chǎn)優(yōu)質(zhì)焊絲/焊條

發(fā)布時間：2015年1月11日   |   閱讀次數(shù)： 735

 一、 鎳基鑄鐵焊條
        Nickel Based Electrode for Cast Iron
        鎳基鑄鐵焊條是修補鑄鐵用的冷焊焊條。藥皮為強還原性石墨型，交直流兩用，電弧穩(wěn)定，可全位置焊接。焊縫金屬具有很好的加工性和承受塑性變形的能力。

牌號 Trade Mark	主要成份(%) Chemical Composition	特性和用途 Characteristics & Application	相當AWS Equivalent to AWS
S201	Sn1 Si0.3 Mn0.3 Cu Rem	機械性能好，抗裂性能好。紫銅氣焊及氬弧焊用。 to gas weld or argon arc weld red copper, and to get good mechanical properties and cracking resistance	ERCu
S211	Si3 Mn1 Cu Rem	機械性能好。銅合金氬弧焊及鋼的MIG釬焊用。 to gas weld copper alloy or to MIG weld steel, and to get good mechanical properties	ERCuSi-A
S212	Sn5 P0.2 Cu Rem	耐磨性好。銅合金氬弧焊及鋼的堆焊用。 to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear	ERCuSn-A
S213	Sn8 P0.2 Cu Rem	耐磨性好。銅合金氬弧焊及鋼的堆焊用。 to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear	ERCuSn-C
S214	Al7.5 Cu Rem	耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用。 to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear and corrosion	ERCuAl-A1
S215	Al9 Cu Rem	耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用。 to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear and corrosion	ERCuAl-A2
S221	Cu60 Sn1 Si0.3 Zn Rem	熔點約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵。 melt at about 890℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well
S221F	Cu60 Sn1 Si0.3 Zn Rem	外涂焊劑的S221焊絲。 S221 welding rod coated with flux
S222	Cu58 Sn0.9 Si0.1 Fe0.8 Zn Rem	熔點約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵。 melt at about 890℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well	RBCuZn-C
S222F	Cu58 Sn0.9 Si0.1 Fe0.8 Zn Rem	外涂焊劑的S222焊絲。 S222 welding rod coated with flux	RBCuZn-C
S223	Cu59 Sn0.6 Zn Rem	熔點約900℃。銅、鋼、鑄鐵釬焊用。 melt at about 900℃ to braze weld copper, steel or cast iro	RBCuZn-A
S224	Cu62 Si0.5 Zn Rem	熔點約905℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵。 melt at about 905℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well
S225	Cu48 Ni10 Zn Rem	熔點約935℃。高強度，釬焊鋼、鎳及硬質(zhì)合金用。 melt at about 935℃ to braze weld steel, nickel or kentanium, and to get high strength	RBCuZn-D
S225F	Cu48 Ni10 Zn Rem	外涂焊劑的S225焊絲。 S225 welding rod coated with flux	RBCuZn-D
S226	Cu60 Sn0.3 Si0.2 Zn Rem	熔點約900℃。黃銅氣焊用，也可釬焊銅、鋼、鑄鐵。 melt at about 900℃ to gas weld bronze copper, and to braze weld copper, steel or cast iron as well
S227	Cu58 Sn0.9 Ni0.5 Si0.1 Fe0.8 Zn Rem	熔點約880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵。 melt at about 880℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well	RBCuZn-B
S229	Cu55 Ni6 Mn4 Zn Rem	熔點約920℃。高強度，釬焊鋼、鎳及硬質(zhì)合金用。 melt at about 920℃ to braze weld steel, nickel or kentanium, and to get high strength

牌號 Trade Mark	主要成份(%) Chemical Composition	特性和用途 Characteristics & Application	相當AWS Equivalent to AWS
S301	SAl 1070	塑性好、耐蝕。純鋁氣焊、氬弧焊用。 to gas weld or argon arc weld aluminum, and to get good ductility and resistance to corrosion	ER1070
ER4043	SAl 4043 (S311)	抗裂性好、通用性大。鋁合金氣焊、氬弧焊用。不宜用于鋁鎂合金。 with a wide range of usage to gas weld or argon arc weld aluminum alloy except magaluma, and to get good cracking resistance	ER4043
ER5183	SAl 5183	耐蝕、強度高。鋁合金氬弧焊用。 to argon arc weld aluminum alloy, and to get resistance to corrosion and high strength	ER5183
ER5356	SAl 5356	耐蝕、強度高，通用性大。鋁合金氬弧焊用。 with a wide range of usage to argon arc weld aluminum alloy, and to get resistance to corrosion and high strength	ER5356
ER5556	SAl 5556 (S331)	耐蝕、強度高。鋁合金氬弧焊用。 to argon arc weld aluminum alloy, and to get resistance to corrosion and high strength	ER5566

牌號 Trade Mark	主要成份(%) Chemical Composition	特性和用途 Characteristics & Application	相當AWS Equivalent to AWS
S111	C1 Cr29 W5 Co Rem	HRc=40~45，高溫下耐磨、耐蝕。堆焊高溫高壓閥門。 apply to resurface and to get resistance to wear and corrosion at high temperature	RCoCr-A
S112	C1.5 Cr29 W8 Co Rem	HRc=45~50，高溫下耐磨、耐蝕。堆焊閥門、熱軋孔型。 apply to resurface and to get resistance to wear and corrosion at high temperature	RCoCr-B
S114	C2.5 Cr30 W12 Co Rem	HRc52，高溫下耐磨、耐熱，但抗沖擊性較差。堆焊牙輪鉆頭。 apply to resurface and to get resistance to wear and corrosion at high temperature, but poor in shock resistance	RCoCr-C
S190	C3.2 Cr27 W14 Co Rem	HRc55，高溫下耐磨、耐熱，但抗沖擊性較差。堆焊牙輪鉆頭。 apply to resurface and to get resistance to wear and corrosion at high temperature, but poor in shock resistance	RCoCr-G